Penetration at 25℃ 100g for 5 seconds |
ASTM D5 |
60-70 Max |
Ductility at 25℃, (77 ℉) 5cm.per min.cm |
ASTM D 113 |
100 min |
Softening Point ℃ |
ASTM D36 |
49-56Max |
Loss on heating, % |
ASTM D6 |
1.0 Max |
Retained penetration at 25℃ 100g for 5second as % of original |
ASTM D5 |
54 Min |
Flash Point (℃) |
ASTM D92 |
250 min |
Solubility in Trichloroethylene, mass % |
ASTM D 2042 |
99.0 Min |
Specific Gravity @25℃ |
ASTM D70 |
1.01 ± 0.05 |
Ductility of residue at 25℃, (77 ℉)5cm.per min.cm |
ASTM D 113-99 |
50 Min |
Drop in penetration after heating% |
ASTM D 5 |
20 Max |
Spot test |
A.A.S.H.T.O.102 |
Negative |
Foam on heating at 175℃ |
ASTM D 92C |
Nil |
Water by distillation, vol% |
ASTM D 95 |
Nil |